Product Description
Pallmann P6 is a powerful, hard and resistant 1-component parquet adhesive, developed according to the latest technologies. This adhesive offers the strength and adhesion of a 2K adhesive, combined with the ease of use of a 1K adhesive. The adhesive is free of solvents and plasticizers, making it a healthy choice for modern applications. Suitable for bonding all common parquet types on various substrates, with hard adhesive beads according to DIN EN 14293.
Suitable for
- Chipboard rolls
- Mosaic
- High Edge
- Tap: 6 mm to 180 mm wide
- Burgundy: 8-10 mm to 240 mm wide
- Planchettes: 10 mm
- Parquet flooring up to 280 mm wide
- Duo plank up to 280 mm wide
- Solid plank up to 140 mm wide (always in combination with intermediate floor)
- Headwood (always in conjunction with UZIN RR188 or UZIN Multimoll fleece)
Suitable on
- Cement screeds, anhydrite floors or concrete
- New screw-down particle board P4-P7 or OSB 2-OSB 4 boards
- Gypsum fiberboards
- Parquet suitable leveling
- Parquet suitable UZIN subfloors
- Hot water floor heating
- Note: All mineral substrates and sanded asphalt floors must be primed with Pallmann P104.
Product Benefits / Features
- Hard, rigid adhesive beads
- Complies with VOC regulations
- Free of plasticizers
- High filling power
- Excellent adhesion of fresh adhesive to cured adhesive
- Fresh glue residues on parquet are removable
- Suitable for underfloor heating
- Solvent-free, contains methoxysilane
- EMICODE EC 1 R PLUS – very low emission
- DE-UZ113 – environmentally friendly and very low emission
Technical data
| Packaging | Plastic bucket |
| Package size | 16 kg |
| Shelf life | At least 6 months |
| Color | Red-brown |
| Consumption | Approx. 800 – 1200 g/m² |
| Minimum application temperature | Floor temperature min. 15 °C |
| Insertion time | Approx. 30 – 45 min* |
| Sandable | After approx. 24 hours*. |
| Overcoatable | After approx. 24 hours* |
| Mechanically loadable | After approx. 12 hours* |
| Final strength | After approx. 3 – 5 days* |
*At 20 °C and 65% relative humidity
Reviews
There are no reviews yet.